Weight %
|
C
|
Mn
|
P
|
S
|
Si
|
Cr
|
Ni
|
|
304L
|
.035
|
2.00
|
.045
|
.030
|
1.00
|
18.0-20.0
|
8.0-13.0
|
|
Grade
|
Tensile
|
||||
|
Ultimate/Min
|
Yield/Min
|
Elongation/Min
|
|||
|
KSI
|
MPA
|
KSI
|
MPA
|
%
|
|
|
304L
|
70
|
485
|
25
|
170
|
35
|
|
Grade
|
Density (kg/m3)
|
Elastic Modulus (GPa)
|
Mean Coefficient of Thermal Expansion (m/m/0C)
|
Thermal Conductivity (W/m.K)
|
Specific Heat 0-1000C (J/kg.K)
|
Electrical Resistivity (n.m)
|
|||
|---|---|---|---|---|---|---|---|---|---|
|
0-1000C
|
0-3150C
|
0-5380C
|
at 1000C
|
at 5000C
|
|||||
|
304/L/H
|
8000
|
193
|
17.2
|
17.8
|
18.4
|
16.2
|
21.5
|
500
|
720
|
|
STANDARD
|
SS 304L
|
|---|---|
|
UNS
|
S30403
|
|
WERKSTOFF NR.
|
1.4306/1.4307
|
|
EN
|
X2CrNi18-9 / X2CrNi19-11
|
|
BS
|
304S11
|
|
GOST
|
03Х18Н11
|
|
JIS
|
SUS 304L
|
|
AFNOR
|
Z3CN18‐10
|